Understanding and Measuring DecarburizationSurface hardness readings were also recorded and results are shown in Fig 3 Note that the specimen austenitized at 1600°F exhibits a large difference be tween surface carbon content and sur face hardness compared to the bar cov ered with mill scale to the descaled one Figure 4 shows results of quantita tive FFD and MAD measurements for the